Stresses in heavy section electroslag joining

Show full item record

Files in this item

Files Size Format Description   View
UBC_1983_A7 I96.pdf 5.390Mb Adobe Portable Document Format   View/Open
 
Title: Stresses in heavy section electroslag joining
Author: Ivo, Paulo Silveira
Degree Master of Applied Science - MASc
Program Metallurgical Engineering
Copyright Date: 1982
Abstract: A study of the thermal stresses resulting in the Electroslag Joining Process as applied to heavy gauge forgings has been undertaken, since a survey of published reports on the process indicates that although solidification cracking ought to be a problem, apparently it is not routinely observed. Welding conditions which are known to produce solidification cracks in Electroslag Welding with wire electrodes were reported to make crack-free welds using ESJ plate electrodes. This study reports work on the thermal and stress fields developed during ESJ of 150 mm thick A36 steel plates. Conditions predicted by previous workers to form cracks with wire electrodes were established and found not to form cracks with plate electrodes. Measurements of stress and temperature during welding were made and found to agree well with a simple numerical model of the process. It is concluded that the thermal field of ESJ is sufficiently different to ESW that it can relax the stress field developed, even in a fully-constrained joint, to the point at which solidification cracking is no longer observed.
URI: http://hdl.handle.net/2429/24079
Series/Report no. UBC Retrospective Theses Digitization Project [http://www.library.ubc.ca/archives/retro_theses/]
Scholarly Level: Graduate

This item appears in the following Collection(s)

Show full item record

All items in cIRcle are protected by copyright, with all rights reserved.

UBC Library
1961 East Mall
Vancouver, B.C.
Canada V6T 1Z1
Tel: 604-822-6375
Fax: 604-822-3893