Properties of polycrystalline GaAs films grown by the close spaced vapour transport technique on Mo substrates Russel, Blair
Abstract
This thesis is a study of the properties of thin GaAs films grown on molybdenum substrates by the close spaced vapour transport (CSVT) deposition technique with the intention that the GaAs/Mo structure would be used as the semiconductor and substrate for economic solar cells. The GaAs films were polycrystalline cubic crystals with no preferred orientation. The crystallite area increased with the temperature at which the substrate was held during growth and at 710°C grain sizes of 100 μm² were observed. The crystallites formed a columnar-like structure with crystal size comparable to the film thickness. No impurities of foreign instrus-ions existed in the films in quantities observable on the electron micro-probe. The resistivity of the GaAs films was 220 Ω cm, hence acceptable for thin film solar cells, however, the GaAs/Mo contact was mildly rectifying. Diodes were fabricated by the deposition of Au onto the GaAs films and the resulting barriers showed values of barrier height of approximately 0.8 eV, ideality factor n = 1.5 to 2, and depletion-layer majority carrier concentration of roughly 10¹⁶ cm⁻³ as measured by J-V and C-V methods. The GaAs films show promise for use in solar cells provided that the Mo/GaAs interface resistance can be reduced.
Item Metadata
Title |
Properties of polycrystalline GaAs films grown by the close spaced vapour transport technique on Mo substrates
|
Creator | |
Publisher |
University of British Columbia
|
Date Issued |
1976
|
Description |
This thesis is a study of the properties of thin GaAs films grown on molybdenum substrates by the close spaced vapour transport (CSVT) deposition technique with the intention that the GaAs/Mo structure would be used as the semiconductor and substrate for economic solar cells. The GaAs films were polycrystalline cubic crystals with no preferred orientation. The crystallite area increased with the temperature at which the substrate was held during growth and at 710°C grain sizes of 100 μm² were observed. The crystallites formed a columnar-like structure with crystal size comparable to the film thickness. No impurities of foreign instrus-ions existed in the films in quantities observable on the electron micro-probe.
The resistivity of the GaAs films was 220 Ω cm, hence acceptable for thin film solar cells, however, the GaAs/Mo contact was mildly rectifying. Diodes were fabricated by the deposition of Au onto the GaAs films and the resulting barriers showed values of barrier height of approximately 0.8 eV, ideality factor n = 1.5 to 2, and depletion-layer majority carrier concentration of roughly 10¹⁶ cm⁻³ as measured by J-V and C-V methods.
The GaAs films show promise for use in solar cells provided that the Mo/GaAs interface resistance can be reduced.
|
Genre | |
Type | |
Language |
eng
|
Date Available |
2010-02-09
|
Provider |
Vancouver : University of British Columbia Library
|
Rights |
For non-commercial purposes only, such as research, private study and education. Additional conditions apply, see Terms of Use https://open.library.ubc.ca/terms_of_use.
|
DOI |
10.14288/1.0093723
|
URI | |
Degree | |
Program | |
Affiliation | |
Degree Grantor |
University of British Columbia
|
Campus | |
Scholarly Level |
Graduate
|
Aggregated Source Repository |
DSpace
|
Item Media
Item Citations and Data
Rights
For non-commercial purposes only, such as research, private study and education. Additional conditions apply, see Terms of Use https://open.library.ubc.ca/terms_of_use.