Low carbon ultrafine grained dual phase steels

Show simple item record

dc.contributor.author Sangem, Vishnu Charan
dc.date.accessioned 2012-05-16T18:36:04Z
dc.date.available 2012-05-16T18:36:04Z
dc.date.copyright 2012 en
dc.date.issued 2012-05-16
dc.identifier.uri http://hdl.handle.net/2429/42328
dc.description.abstract Ultrafine grained (UFG) (i.e. grain size of the order 1 µm) dual phase (DP) steels have been investigated using a thermo-mechanical process designed to obtain fine ferrite-carbide aggregates prior to intercritical annealing. The effects of carbon content, alloying additions, initial starting structures and processing parameters like heating and cooling rate on the mechanical properties have been quantified. Experimental work was conducted on two plain low carbon steels (0.06 and 0.12 wt pct C) and two low carbon (0.06 wt pct) micro-alloyed steels, one with Mo (0.15 wt pct) and the other with Nb (0.06 wt pct) addition, respectively. Fine ferrite-carbide aggregates were obtained only for the plain carbon steels and not for the micro-alloyed steels; hence no further studies are carried out for the micro-alloyed steels. A Gleeble 3500 thermomechanical simulator is used for the intercritical annealing operation to obtain UFG DP steels. The tensile test results showed that a critical carbon (about 0.1 wt pct) content may be necessary for obtaining a good balance of strength and ductility. The lower carbon steels showed better true strain to fracture behavior, but fall behind in terms of strength and ductility compared to the higher carbon steel. Higher heating rates are necessary for achieving fine microstructures as well as better mechanical properties, whereas lower heating rates helped in obtaining good strength-elongation (engineering tensile strength × uniform elongation) balance. For the sake of comparison martensite starting structures are also used to obtain UFG DP steels. There is no effect of heating rate on the strength values, but higher heating rates resulted in better elongation as well as fracture strain values. Overall, the UFG DP steels fabricated by using martensite starting structures showed better strength-elongation balance, moreover the number of processing steps are considerably reduced. en
dc.language.iso eng en
dc.publisher University of British Columbia en
dc.relation.ispartof Electronic Theses and Dissertations (ETDs) 2008+ en
dc.rights Attribution-NonCommercial 2.5 Canada
dc.rights.uri http://creativecommons.org/licenses/by/3.0/
dc.title Low carbon ultrafine grained dual phase steels en
dc.type Text en
dc.degree.name Master of Applied Science - MASc en
dc.degree.discipline Materials Engineering en
dc.degree.grantor University of British Columbia en
dc.date.graduation 2012-11 en
dc.type.text Thesis/Dissertation en
dc.description.affiliation Applied Science, Faculty of
dc.degree.campus UBCV en
dc.description.scholarlevel Graduate en

Files in this item

Files Size Format Description   View
ubc_2012_fall_sangem_vishnu.pdf 4.892Mb Adobe Portable Document Format   View/Open

This item appears in the following Collection(s)

Show simple item record

All items in cIRcle are protected by copyright, with all rights reserved.

Attribution-NonCommercial 2.5 Canada Except where otherwise noted, this item's license is described as Attribution-NonCommercial 2.5 Canada

UBC Library
1961 East Mall
Vancouver, B.C.
Canada V6T 1Z1
Tel: 604-822-6375
Fax: 604-822-3893